Deposition and characterization of nitrogen containing stainless steel coatings prepared by reactive magnetron sputtering
(1996)
Nitrogen containing austenitic stainless steel coatings were deposited with nitrogen concentrations up to 14.1 at% using electron enhanced closed field unbalanced DC magnetron sputtering. The reactive gas flow was controlled ...
Structure, hardness and mechanical properties of magnetron-sputtered titanium-aluminium boride films
(1999)
TiAlB films nominally 2 μm thick were produced by simultaneous sputtering from TiAl and TiB2 targets onto Si-(110) and AISI316 stainless steel substrate materials at a temperature of 170°C. The influence of different B/Al ...
Textured VN coatings with Ag3VO4 solid lubricant reservoirs
(2011)
Silver oxovanadate powders were produced using a low temperature hydrothermal synthesis method. X-ray diffraction (XRD) and Raman microscopy revealed the formation of the α-Ag3VO4 phase, and differential scanning calorimetry ...
Partially yttria-stabilized zirconia coatings produced under plasma-assisted EBPVD with bipolar pulsed bias and under electron bombardment-assisted positive bias conditions
(1997)
Previous research using radio frequency (rf) plasma-assisted electron beam (EB) PVD to deposit partially yttria-stabilized zirconia (PYSZ) thermal barrier coatings has shown the benefits of this method in terms of structure ...
Composite DLC-metal/metal-carbide coatings produced by electron enhanced unbalanced magnetron sputtering
(1997)
Composite coatings consisting of metal containing diamond like carbons were produced by unbalanced magnetron sputtering in a closed field magnetic configuration. Targets of Pta and W were poisoned with acetylene during the ...
Wear behaviour of carbon-containing tungsten coatings prepared by reactive magnetron sputtering
(1999)
W(1-x)C(x) coatings (with x being in the range of 0.05-0.19) were deposited by reactive magnetron sputtering on to AISI 316 stainless-steel substrates in order to study the influence of the carbon content on the tribological ...
Structure, mechanical and tribological properties of sputtered TiAlBN thin films
(1999)
TiAlBN films were produced by simultaneously sputtering from TiAl and TiB2 targets in Ar/N2 mixtures at a substrate temperature of 150 °C. The goal of this investigation was to study the influence of the nitrogen content ...
Deposition and characterisation of carbon-containing tungsten coatings prepared by reactive magnetron sputtering
(1998)
Carbon-containing tungsten coatings were deposited by magnetron sputtering onto AISI 316 stainless steel substrates in Ar/C2H2 gas mixtures. Optical emission spectroscopy was used to control the C2H2 gas flow. The goal of ...
X-Ray diffraction investigations of magnetron sputtered TiCN coatings
(1995)
X-ray diffraction measurements were performed on titanium carbonitride coatings produced in an electron enhanced, unbalanced magnetron system. The films were deposited onto AISI 316 stainless steel substrates with an argon ...
Microstructural and morphological effects on the tribological properties of electron enhanced magnetron sputtered hard coatings
(1995)
X-ray diffraction measurements and scanning electron microscopy studies on close to stoichiometric titanium carbonitride [TiCxN(1 _x)] and carbon containing tungsten coatings produced in an electron enhanced unbalanced ...