Low-temperature water-gas shift on Pt/Ce1-xLaxO2-δ: Effect of Ce/La ratio
ΣυγγραφέαςPetallidou, Klito C.
Efstathiou, Angelos M.
SourceApplied Catalysis B: Environmental
Google Scholar check
MetadataΕμφάνιση πλήρους εγγραφής
Pt nanoparticles (1.0-1.4nm size) supported on Ce1-xLaxO2-δ (x=0.0, 0.2, 05, 0.8 and 1.0) carriers, the latter prepared by the citrate sol-gel method, were tested toward the water-gas shift (WGS) reaction in the 200-400°C range. A deep insight into the effect of Ce/La atom ratio of support chemical composition on the catalytic performance (CO conversion vs. temperature and stability) and kinetic rates of Pt-loaded catalysts was realized after employing HAADF/STEM, in situ Raman and DRIFT spectroscopies under different gas atmospheres, temperature-programmed surface reaction (TPSR) in He and O2/He gas atmospheres following WGS reaction, CO-TPD, in situ UV-vis/DRS, oxygen storage capacity measurements, and transient 18O-isotopic exchange studies followed by WGS reaction. It was found that doping of ceria with 20at.% La3+ has increased significantly the catalytic activity of 0.5wt% Pt/Ce0.8La0.2O2-δ solid in the 250-350°C range, whereas addition of 50-80at.% La3+ in ceria caused a negative effect on the CO conversion with respect to pure ceria. It was found that the Ce/La atom ratio in Ce1-xLaxO2-δ influences the catalytic site reactivity (k) along the Pt-support interface. The optimum La3+-dopant concentration of 20at.% (Ce/La=4/1) used in Pt/Ce0.8La0.2O2 compared to the worst one of 80at.% (Pt/Ce0.2La0.8O2-δ, Ce/La=1/4) correlates with (i) the higher specific kinetic rate per length of Pt-support interface (μmol COcm-1s-1), (ii) the higher concentration of oxygen vacant sites, (iii) the lower amount (μmol/g-1) of "carbon" accumulated during WGS and best stability with time on stream, (iv) the lower apparent activation energy (kcalmol-1) of WGS reaction, (v) the lower degree toward Pt oxidation (largest Pt2+/Pt4+ ratio), (vi) the lower Ce1-xLaxO2-δ support energy band gap, and (vii) the lower mobility of surface lattice oxygen. © 2013 Elsevier B.V.
Showing items related by title, author, creator and subject.
Zeinalipour-Yazdi, Constantinos D.; Efstathiou, Angelos M. (2008)In this work, a detailed first principle study of the mechanism of the heterogeneous catalytic water-gas shift (WGS) reaction on a rhodium cluster is presented. A large number of possible reaction mechanisms relevant to ...
Effects of reaction temperature and support composition on the mechanism of water - Gas shift reaction over supported-Pt catalysts Kalamaras, Christos M.; Gonzalez, I. D.; Navarro, R. M.; Fierro, José Luis García; Efstathiou, Angelos M. (2011)The present work reports on a detailed study of the effect of support chemical composition and reaction temperature on the mechanism of the water-gas shift (WGS) reaction over supported-Pt catalysts. The effect of the same ...
The effect of La3+-doping of CeO2 support on the water-gas shift reaction mechanism and kinetics over Pt/Ce1-xLaxO2-δ Kalamaras, Christos M.; Petallidou, Klito C.; Efstathiou, Angelos M. (2013)Platinum nanoparticles (dPt=1.0-1.2nm) supported on single CeO2 and La2O3 metal oxides and Ce0.8La0.2O2-δ solid solution were prepared to investigate for the first time the effect of La3+-doping of ceria on important ...