Ultraviolet emission from low resistance Cu2SnS3/SnO2 and CuInS2/Sn:In2O3 nanowires
Date
2014ISSN
2166-532XSource
APL MaterialsVolume
2Issue
11Google Scholar check
Metadata
Show full item recordAbstract
SnO2 and Sn:In2O3 nanowires were grown on Si(001), and p-n junctions were fabricated in contact with p-type Cu2S which exhibited rectifying current-voltage characteristics. Core-shell Cu2SnS3/SnO2 and CuInS2/Sn:In2O3 nanowires were obtained by depositing copper and post-growth processing under H2S between 100 and 500°C. These consist mainly of tetragonal rutile SnO2 and cubic bixbyite In2O3. We observe photoluminescence at 3.65 eV corresponding to band edge emission from SnO2 quantum dots in the Cu2SnS3/SnO2 nanowires due to electrostatic confinement. The Cu2SnS3/SnO2 nanowires assemblies had resistances of 100 Ω similar to CuInS2/In2O3 nanowires which exhibited photoluminescence at 3.0 eV. © 2014 Author(s).