The nanostructure, wear and corrosion performance of arc-evaporated CrBxNy nanocomposite coatings
(2009)
The composition, nanostructure, tribological and corrosion behaviour of reactive arc evaporated CrBxNy coatings have been studied and compared to CrN. The CrBxNy coatings were deposited on a commercial Oerlikon Balzers RCS ...
Tribological properties of twin electron-beam evaporated Cr-N and Al-Cr-N coatings under laboratory sliding and drill experiments
(2008)
The tribological behavior of substoichiometric Cr-N and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was studied. Al-Cr-N coatings with Al to Cr ratios in the range of 1-8 (and nitrogen concentrations ...
Adaptive VN/Ag nanocomposite coatings with lubricious behavior from 25 to 1000 °c
(2010)
A two-phase nanocomposite coating that consists of inclusions of silver in a vanadium nitride matrix (VN/Ag) was investigated as a potential adaptive coating with a reduced friction coefficient from 25 to 1000 °C. This ...
Evaluating the microstructure and performance of nanocomposite PVD TiAlBN coatings
(2002)
Physical vapour deposition (PVD) TiAlBN coatings can exhibit excellent wear resistance, with optimised coating compositions demonstrating a 150% increase in lifetime compared to standard TiAlN coatings in wet-cutting drill ...
Electron spectroscopic studies of nanocomposite PVD TiAlBN coatings
(2002)
A range of TiAlBN coatings have been deposited by electron beam evaporation and the optimised composition exhibits a 150% improvement over single phase TiAlN coatings in drilling tests. The coatings have been analysed by ...
Tribological behavior of CrN and Al-Cr-N coatings
(Affiliation: Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United StatesAffiliation: Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678, Nicosia, CyprusCorrespondence Address: Demas, N. G.Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United States, 2009)
The tribological behavior of CrN and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was investigated. The composition, structure, mechanical and tribological properties of the coatings were determined ...
Few-layer graphene-like flakes derived by plasma treatment: A potential material for hydrogen adsorption and storage
(2016)
A novel, one-step, wet-free, environmental friendly and high-yield method for producing few-layer graphene powders with large surface areas (up to 800 m2/g) and narrow nanopore sizes (0.7-0.8 nm) using plasma-induced ...
Nanostructural studies of PVD TiAlB coatings
(2006)
TiAlB coatings with different compositions were deposited by co-sputtering from TiAl and TiB2 targets onto AISI316 stainless steel substrates at a temperature of 170 °C. The stoichiometry and nanostructure have been studied ...
Synthesis and characterization of Cr-B-N coatings deposited by reactive arc evaporation
(2008)
Nanocomposite Cr-B-N coatings were deposited from CrB0.2 compound targets by reactive arc evaporation using an Ar/N2 discharge at 500 °C and -20 V substrate bias. Elastic recoil detection (ERDA), x-ray photoelectron ...
Nanostructure, mechanical and tribological properties of reactive magnetron sputtered TiCx coatings
(2008)
This study describes the correlation between microstructure, mechanical and tribological properties of TiCx coatings (with x being in the range of 0-1.4), deposited by reactive magnetron sputtering from a Ti target in ...