Tribological properties of twin electron-beam evaporated Cr-N and Al-Cr-N coatings under laboratory sliding and drill experiments
(2008)
The tribological behavior of substoichiometric Cr-N and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was studied. Al-Cr-N coatings with Al to Cr ratios in the range of 1-8 (and nitrogen concentrations ...
Tribological behavior of CrN and Al-Cr-N coatings
(Affiliation: Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United StatesAffiliation: Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678, Nicosia, CyprusCorrespondence Address: Demas, N. G.Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United States, 2009)
The tribological behavior of CrN and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was investigated. The composition, structure, mechanical and tribological properties of the coatings were determined ...
Nanostructure, mechanical and tribological properties of reactive magnetron sputtered TiCx coatings
(2008)
This study describes the correlation between microstructure, mechanical and tribological properties of TiCx coatings (with x being in the range of 0-1.4), deposited by reactive magnetron sputtering from a Ti target in ...
Effect of Cu content on the tribological performance of Cr-N coatings at high temperatures (840°C)
(Affiliation: Department of Mechanical and Manufacturing Eng., University of Cyprus, Nicosia, CyprusAffiliation: Department of Mechanical Science and Eng., University of Illinois at Urbana-Champaign, Urbana, IL, United StatesAffiliation: Institute for Health and Consumer Protection, Joint Res. Centre of the European Commission, Ispra (VA), ItalyCorrespondence Address: Polychronopoulou, K.Department of Mechanical and Manufacturing Eng., University of Cyprus, Nicosia, Cyprus, 2010)
Cr-N and Cu-Cr-N coatings with Cu content between 3-65 at.%, Cu/Cr ratios in the 0.04-4.5 range and 21-27 at.% N, synthesized by twin e-beam Physical Vapor Deposition (EBPVD) at 450°C, were investigated. Using X-ray ...